ABS+PC FR 110 DATASHEET
ABS+PC FR 110 DATASHEET
Technical Data | ||
Product Description | ||
ABS/PC FR 110: a fire-resistant thermoplastic blend plastic offering excellent mechanical properties and versatile applications. Multiple custom colors are available in neway plastic injectin molding. Learn more now! | ||
Physical | Nominal Value Unit | Test Method |
Specific Gravity | 1.19g/cm3 | ASTM D792 |
Melt Mass-Flow Rate (MFR) (240°C/5.0 kg) | 20g/10 min | ASTM D1238 |
Molding Shrinkage - Flow | 0.40 to 0.60 % | ASTM D955 |
Water Absorption (Saturation, 73°F (23°C)) | 0.050% | ASTM D570 |
Spiral Flow Length | Internal Method | |
490°F (254°C), 0.10in (2.54 mm) | 584 mm | |
Mechanical | Nominal Value Unit | lest Method |
Tensile Modulus | 2620 MPa | ASTM D638 |
Tensile Strength | ASTM D638 | |
Yield | 60.0 MPa | |
Break | 49.6 MPa | |
Tensile Elongation | ASTM D638 | |
Yield | 4.0% | |
Break | >50% | |
Flexural Modulus | 2690 MPa | ASTM D790 |
Flexural Strength (5.0% Strain) | 95.1 MPa | ASTM D790 |
Impact | Nominal Value Unit | Test Method |
Notched Izod Impact | ASTM D256 | |
73°F (23°C), 0.125 in (3.18 mm) | 750J/m | |
Instrumented Dart Impact2,3 | ASTM D3763 | |
0.125 in (3.18 mm), Total Energy | 51.5J | |
Hardness | Nominal Value Unit | Test Method |
Rockwell Hardness (R-Scale) | 122 | ASTM D785 |
Thermal | Nominal Value Unit | Test Method |
Deflection Temperature Under Load | ASTM D648 | |
66 psi (0.45 MPa), Unannealed, 0.250 in (6.35mm) | 100 °C | |
264 psi (1.8 MPa), Unannealed, 0.250 in (6.35mm) | 95 °C | |
Vi cat Softening Temperature | 110 °C | ISO 306/B120 |
CLTE - Flow | 0.000077 cm/cm/°C | ASTM D696 |
Electrical | Nominal Value Unit | Test Method |
Surface Resistivity | > 1.0E+14ohms | IEC 60093 |
Volume Resistivity | > 1.0E+13 ohmcm | ASTM D257 |
Relative Permittivity | IEC 60250 | |
100 Hz | 3.20 | |
1 MHz | 3.10 | |
Dissipation Factor | IEC 60250 | |
100 Hz | 0.0030 | |
1 MHz | 0.0080 | |
Comparative Tracking Index | 350 V | IEC 60112 |
Electric Strength | 30 kV/mm | IEC 60243-1 |
Flammability | Nominal Value Unit | Test Method |
Flame Rating - UL | UL94 | |
0.0787 in (2.00 mm) | 5VB | |
0.118 in (3.00 mm) | 5VA | |
Oxygen Index | 30% | ASTM D2863 |
Injection | Nominal Value Unit | |
Drying Temperature | 79.4 °C | |
Drying Time | 4.0hr | |
Suggested Max Moisture | 0.020% | |
Suggested Max Reg rind | 20% | |
Rear Temperature | 221 to 229 °C | |
Middle Temperature | 224 to 235 °C | |
Front Temperature | 229 to 241 °C | |
Nozzle Temperature | 252 to 263 °C | |
Processing (Melt) Temp | 221 to 271 °C | |
Mold Temperature | 60.0 to 79.4 °C | |
Injection Pressure | 68.9 to 110MPa | |
Injection Rate | Slow-Moderate | |
Back Pressure | 0.345 to 0.689 MPa | |
Screw Speed | 40 to 70rpm | |
Clamp Tonnage | 4.1 to6.9kN/cm2 | |
Cushion | 3.18 to 6.35mm | |